Method of manufacturing a semiconductor integrated circuit device having a columnar laminate

ABSTRACT

For improving the filling properties between vertical MISFETs constituting a SRAM memory cell, the vertical MISFETs are formed over horizontal drive MISFETs and transfer MISFETs, and they are disposed with a narrow pitch in the Y direction and a wide pitch in the X direction. After a first insulating film (O 3 -TEOS) having good coverage is disposed over a columnar laminates having a lower semiconductor layer, an intermediate semiconductor layer, an upper semiconductor layer and a silicon nitride film and a gate electrode formed over the side walls of the laminates via a gate insulating film to completely fill a narrow pitch space, a second insulating film (HDP silicon oxide film) is deposited over the first insulating film, resulting in an improvement in the filling properties, even in a narrow pitch portion, between vertical MISFETs having a high aspect ratio.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. application Ser. No.11/651,095, filed Jan. 9, 2007, which, in turn is a divisional of U.S.application Ser. No. 10/756,419, filed Jan. 14, 2004 (now U.S. Pat. No.7,259,052), and which application claims priority from Japanese PatentAppln. 2003-005825, filed Jan. 14, 2003, the entire contents of whichare incorporated herein by reference.

TECHNICAL FIELD

The present invention relates to a semiconductor integrated circuitdevice and to a technique for use in the manufacture thereof; and, moreparticularly, the invention relates to a technique that is effectivewhen applied to a semiconductor integrated circuit device having avertical MISFET.

BACKGROUND OF THE INVENTION

Semiconductor integrated circuit devices have many layer-stackstructures, each having a conductive film and an insulating film. Theinsulating film tends to be formed in order to insulate betweenconductive films. For example, plural interconnect layers are separatedby an insulating film. An element formation region of a semiconductorsubstrate is also separated by an insulating film that has been filledin a groove.

The space between interconnects or a groove space, however, tends to benarrower with a recent tendency toward high integration andminiaturization of the device. In some parts, the ratio of the width tothe height of a space (aspect ratio=height/width) becomes large.

Various improvements have been made to fill such a space accurately. Forexample, the below-listed Patent Document 1 discloses a technique whichinvolves filling a first insulating film (46) in a region having a fineline width and a high height/width ratio, for example, a space betweenconductive lines (42), carrying out dry etch back (50) to remove voids(48), and then forming a second insulating film (52) over the firstinsulating film.

Patent Document 1: Japanese Patent Laid-Open No. Hei 11 (1999)-176936

SUMMARY OF THE INVENTION

The present inventors have been engaged in research and development ofsemiconductor integrated circuit devices. They have carried out aninvestigation particularly directed to the structure or manufacturingmethod of an SRAM (Static Random Access Memory), which is a kind ofsemiconductor memory device.

With regards to the SRAM investigated by the present inventors, itsmemory cell is formed of, for example, four n-channel type MISFETs(Metal-Insulator-Semiconductor-Field-Effect-Transistor) and two pchannel type MISFETS.

Since a reduction in the memory size cannot be attained easily whenthese six MISFETs constituting the memory cell of the SRAM are disposedon the same plane, the formation of two vertical p channel type MISFETsover the four horizontal type MISFETs, which will be described later,has been under investigation. It has been revealed that when verticaltype MISFETs are employed, it becomes difficult to fill an insulatingfilm between them. More specifically, a vertical type MISFET is made ofa columnar semiconductor having source and drain regions thereover andtherebelow, respectively. The ratio (aspect ratio) of the height of thiscolumnar semiconductor to the space between two adjacent columnarsemiconductors is much greater than the aspect ratio of the spacebetween interconnects or that of an element isolation groove which hasbeen studied conventionally. It is therefore necessary to develop atechnique that is capable of filling a space between columnarsemiconductors with good accuracy.

In particular, when the distance between two columnar semiconductors inthe X direction is different from that in the Y direction inconsideration of the layout of underlying horizontal MISFETs andvertical MISFETs, it is necessary to fill the space with good accuracy,whether it is narrow or wide.

An object of the present invention is to provide a technique that iscapable of improving the filling properties in a space between verticalMISFETs constituting a semiconductor integrated circuit device.

Another object of the present invention is to improve the properties ofa semiconductor integrated circuit device having vertical MISFETs, andalso to attain miniaturization of the device.

The above-described and the other objects and novel features of thepresent invention will be more apparent from the description-providedherein and from the accompanying drawings.

An outline of typical aspects of the invention disclosed in the presentapplication will be described below.

In one aspect of the present invention, there is provided asemiconductor integrated circuit device comprising a plurality ofvertical MISFETs having (a1) a columnar laminate having, at the upperportion and lower portion thereof, first and second semiconductorregions, respectively, and (a2) a conductive film formed over side wallsof the columnar laminate via a first insulating film, wherein theplurality of vertical MISFETs having the columnar laminate and theconductive film are (b1) spaced by a first distance in a firstdirection, and (b2) spaced by a second distance greater than the firstdistance in a second direction; and, up to at least a predeterminedheight of the columnar laminate of each of the plurality of verticalMISFETs, (c1) a second insulating film is formed in the space of thecolumnar laminates in the first direction, and (c2) the secondinsulating film and a third insulating film thereover are formed in thespace of the columnar laminates in the second direction.

In a second aspect of the present invention, there is provided a methodof manufacture of a semiconductor integrated circuit device, comprisingthe steps of (a) forming a plurality of columnar laminates having, atthe upper portion and lower portion thereof, first and secondsemiconductor regions, respectively, while spacing the columnarlaminates in a first direction and in a second direction with a space inthe second direction being wider than that in the first direction; (b)forming a conductive film over the side walls of each of the columnarlaminates via a first insulating film and setting a distance, in thefirst direction, between the conductive films over the side walls of thecolumnar laminates as a first distance, and a distance in the seconddirection as a second distance greater than the first distance; (c)forming a second insulating film to be thick enough to fill the firstdistance, but not the second distance; and (d) forming a thirdinsulating film over the second insulating film, while filling thesecond distance.

In a third aspect of the present invention, there is provided a methodof manufacture of a semiconductor integrated circuit device, whichcomprises the steps of (a) forming a semiconductor film having, at theupper portion and lower portion thereof, first and second semiconductorregions, respectively; (b) etching the semiconductor film with a maskwhich is H-shaped in a first direction, thereby forming an approximatelyelliptical columnar laminate having a longer diameter in a seconddirection that is perpendicular to the first direction; and (c) forminga conductive film over the side walls of the columnar laminate via aninsulating film.

In a fourth aspect of the present invention, there is provided asemiconductor integrated circuit device comprising (a) a columnarlaminate having, at the upper and lower portions thereof, first andsecond semiconductor regions, respectively, and having a substantiallyelliptical columnar plane pattern; and (b) a conductive film formed overthe side walls of the columnar laminate via an insulating film.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an equivalent circuit diagram of a SRAM memory cell accordingto one embodiment of the present invention;

FIG. 2 is a fragmentary cross-sectional view of a substrate illustratinga manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 3 is a fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 4 is a fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 5 is fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 6 is a fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 7 is a fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 8 is a fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 9 is a fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 10 is a fragmentary cross-sectional view of a substrateillustrating the manufacturing method of the semiconductor integratedcircuit device (SRAM) according to the one embodiment of the presentinvention;

FIG. 11 is a fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 12 is a plan view illustrating a transfer pattern (reticle pattern)to be used for a manufacturing step of the semiconductor integratedcircuit device (SRAM) according to the one embodiment of the presentinvention;

FIG. 13 is a table illustrating the relationship between the transferpattern and an etched shape (plane pattern of laminate);

FIG. 14 is a fragmentary cross-sectional view of a substrateillustrating the manufacturing method of the semiconductor integratedcircuit device (SRAM) according to the one embodiment of the presentinvention;

FIG. 15 is a fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 16 is a fragmentary cross-sectional view of a substrateillustrating the manufacturing method of the semiconductor integratedcircuit device (SRAM) according to the one embodiment of the presentinvention;

FIG. 17 is a fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 18 is a fragmentary cross-sectional view of a substrateillustrating the manufacturing method of the semiconductor integratedcircuit device (SRAM) according to the one embodiment of the presentinvention;

FIG. 19 is a fragmentary perspective view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 20 is a fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 21 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 22 is a fragmentary perspective view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 23 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 24 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 25 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 26 is a fragmentary perspective view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 27 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 28 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 29 is fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 30 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 31 is fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 32 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 33 is fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 34 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 35 is a fragmentary plan view of a substrate of the semiconductorintegrated circuit device (SRAM) according to the one embodiment of thepresent invention;

FIG. 36 is a fragmentary layout diagram of a substrate of thesemiconductor integrated circuit device (SRAM) according to the oneembodiment of the present invention;

FIG. 37 is a fragmentary plan view of a substrate of the semiconductorintegrated circuit device (SRAM) according to the one embodiment of thepresent invention;

FIG. 38 is fragmentary plan view of a substrate illustrating themanufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 39 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) according to the one embodiment of the present invention;

FIG. 40 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) for describing the advantages of the one embodiment of thepresent invention;

FIG. 41 is fragmentary cross-sectional view of a substrate illustratingthe manufacturing method of the semiconductor integrated circuit device(SRAM) for describing the advantages of the one embodiment of thepresent invention;

FIG. 42 is an equivalent circuit diagram of another SRAM memory cellaccording to the one embodiment of the present invention;

FIG. 43 is a fragmentary plan view of a substrate illustrating the othersemiconductor integrated circuit device (SRAM) according to the oneembodiment of the present invention;

FIG. 44 is a fragmentary cross-sectional view of a substrateillustrating the other semiconductor integrated circuit device (SRAM)according to the one embodiment of the present invention;

FIG. 45 is a fragmentary plan view of a substrate illustrating the othersemiconductor integrated circuit device (SRAM) according to the oneembodiment of the present invention; and

FIG. 46 is a fragmentary cross-sectional view of a substrateillustrating a further semiconductor integrated circuit device (SRAM)according to the one embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The embodiments of the present invention will hereinafter be describedspecifically with reference to the accompanying drawings. In all of thedrawings, members having a like function will be identified by likereference numerals and overlapping descriptions thereof will be omitted.To facilitate an understanding of the description, some parts (forexample, an insulating film) will be described with reference to anordinal number “first”, “second” or the like, but this does not alwayscorrespond to the terms “first”, “second” or the like as used in theappended claims.

FIG. 1 is an equivalent circuit diagram of a memory cell of a SRAMaccording to an embodiment of the present invention. As illustrated inFIG. 1, memory cells (MC) of the SRAM are each constituted of twohorizontal transfer MISFETs (TR1 and TR2, each of which will hereinaftersimply be called a “transfer MISFET”), two horizontal drive MISFETs (DR1and DR2, each of which will hereinafter simply be called a “driveMISFET”), and two vertical load MISFETs (SV1 and SV2, each of which willhereinafter simply be called a “vertical MISFET”), each disposed at theintersection of a pair of complementary data lines (BLT and BLB) and aword line (WL).

Of the six MISFETs constituting the memory cell (MC), two transferMISFETs (TR1 and TR2) and two drive MISFETs (DR1 and DR2) are eachformed as an n channel type MISFET. The two vertical MISFETs (SV1 andSV2) are each formed as a p channel type MISFET.

As will be described later, the vertical MISFETs (SV1 and SV2) aredisposed over formation regions of the drive MISFETs (DR1 and DR2) andtransfer MISFETs (TR1 and TR2).

As illustrated in FIG. 1, the drive MISFET (DR1) and the vertical MISFET(SV1) of the memory cell (MC) constitute a first inverter INV₁, whilethe drive MISFET (DR2) and the vertical MISFET (SV2) constitute a secondinverter INV₂. The input and output portions for the pair of invertersINV₁ and INV₂ are crosslinked within the memory cell (MC) and constitutea flip flop circuit, which serves as an information storing unit forstoring information of 1 bit.

More specifically, two pairs of MISFETs constituting the inverter areconnected in series between a reference voltage (Vss) and a supplyvoltage (Vdd, for example, 3V) and the connecting nodes (output portion,A and B) are cross-connected to the connecting portions (input portions)of these gate electrodes.

In other words, the drain (one end) of the drive MISFET (DR1), the drainof the vertical MISFET (SV1), the gate of the drive MISFET (DR2) and thegate of the vertical MISFET (SV2) are electrically connected each other.

Each portion of these MISFETs is connected to one storage node (A) ofthe memory cell. The drain of the drive MISFET (DR2), the drain of thevertical MISFET (SV2), the gate of the drive MISFET (DR1) and the gateof the vertical MISFET (SV1) are electrically connected each other. Eachportion of these MISFETs is connected to one storage node (B) of thememory cell.

Between the storage nodes (A and B) and the complementary data lines(BLT and BLB), the transfer MISFETs (TR1 and TR2) are electricallyconnected, respectively. The gate electrodes of the transfer MISFETS(TR1 and TR2) are electrically connected to the word line (WL). Theabove-described memory cell (MC) stores data by setting the potential ofone of the paired storage nodes (A and B) high (High) and that of theother one low (Low).

Upon reading of the data of the memory cell (MC), the supply voltage(Vdd) is applied to a selected word line (WL) to turn the transferMISFETS (TR1 and TR2) ON and a potential difference between the pairedstorage nodes (A and B) is read via the complementary data lines (paireddata lines BLT and BLB).

Upon writing, the supply voltage (Vdd) is applied to a selected wordline (WL) to turn the transfer MISFETS (TR1 and TR2) ON, and, at thesame time, one of the complementary data lines (BLT and BLB) isconnected to the supply voltage (Vdd), while the other is connected tothe reference voltage (Vss), whereby the ON and OFF sates of the driveMISFETs (DR1 and DR2) are inverted.

FIGS. 2 to 34 (except FIGS. 12 and 13) are a fragmentary cross-sectionalview, fragmentary plan view or fragmentary perspective view of asubstrate illustrating a method of manufacture of the semiconductorintegrated circuit device (SRAM) according to this embodiment. In eachcross-sectional view, a diagram on the left side is a view taken along aline A-A′ of the plan view, a diagram at the center is a view takenalong a line B-B′ of the plan view and a view on the right side is aview taken along a line C-C′ of the plan view.

The characteristic structure of the semiconductor integrated circuitdevice (SRAM) according to this embodiment will be described next. Itsdetailed structure will be described in accordance with the successivemanufacturing steps used in the fabrication thereof.

As illustrated in FIGS. 33 and 34, which are views of the final step,the SRAM memory cell is formed in a substantially rectangular cellregion surrounded by the mark (+) in the diagram; the drive MISFETs (DR1and DR2) and transfer MISFETs, which are horizontal transistors, areformed in a relatively lower-layer region; and the vertical MISFETs (SV1and SV2) are formed in a region above the above-described four regions.

What is characteristic in the SRAM of this embodiment is that a spacebetween SV1 and SV2 of the vertical MISFET in the Y direction (adirection of B-B′) is, as illustrated in the center diagram of FIG. 34,filled with a single layer of a first insulating film (O₃-TEOS film) 70a up to the vicinity of the upper portion of its gate electrode 66,while a space in the X direction has a stacked structure of a firstinsulating film (O₃-TEOS film) 70 a and a second insulating film (HDPoxide film) 70 b.

As illustrated in FIG. 35, cell regions are disposed in an array in Xand Y directions, and each cell region is disposed axisymmetric to ashort side of the cell region running in the Y direction andaxisymmetric to a long side of the cell region running in the Xdirection. Each pattern in the cell region is disposed point-symmetricto the central point of the cell region.

The vertical MISFETs (SV1 and SV2) are therefore disposed in an array inthe X and Y directions. They are spaced by a distance D1 in the Ydirection and with a distance D2 (D2>D1) in the X direction. In FIG. 35,some of the patterns (SV1, SV2, 42, 43 and the like) shown in FIG. 33are also shown.

With regard to the positional relationship between the vertical MISFETs(columnar laminates (P1 and P2) and gate electrode 66) disposed in thearray form and the first insulating film 70 a, the columnar laminates(P1 and P2) and the gate electrodes 66 that are arranged in the Ydirection seem to be embedded in a projecting portion 172 a extending inthe Y direction of the first insulating film (O₃-TEOS film) 70 a (referto FIG. 26).

Between the projecting portions extending in the direction Y of thefirst insulating film (O₃-TEOS film) 70 a, a second insulating film (HDPoxide film) 70 b is filled (refer to FIG. 26). The columnar laminates(P1 and P2) that protrude from the first insulating film (O₃-TEOS film)70 a are covered with a fourth insulating film (P-TEOS film) 73 (referto FIG. 34).

The plane pattern of each of the columnar laminates (P1 and P2) whichare disposed in an array can be formed, as illustrated in FIG. 17, to beapproximately elliptic. The longer diameter of this approximatelyelliptic pattern is located in a long-side direction (X direction) ofthe cell region.

By forming the approximately elliptical pattern of the columnarlaminates (P1 and P2) to be longer in the direction in which they arespaced widely (with a wide pitch), the channel region can be widened andthe channel current can be increased. In addition, a size reduction inthe cell region can be attained.

A specific example of the structure of the semiconductor integratedcircuit device (SRAM) according to this embodiment will be described indetail in the order of the manufacturing steps.

As illustrated in FIGS. 2 and 3, an element isolation is formed in asubstrate 1 made of, for example, p type single crystal silicon. Thiselement isolation is formed by, for example, making a groove 2 in thesubstrate 1, thermally oxidizing the resulting substrate, and thenfilling a silicon oxide film 3 in the groove as an insulating film. Anexposed region of the substrate 1 surrounded by this element isolationwill be an element formation region (active region) L.

Into a part of the substrate 1, a p type impurity (for example, boron(B) is ion-implanted and thermally diffused, whereby a p type well 4 isformed over the main surface of the substrate 1.

The region shown in FIGS. 2 and 3 is a memory region around which aperipheral circuit region exists, though this is not illustrated. Inaddition to the p type well, an n type well is formed in this peripheralcircuit region by diffusion of an n type impurity. Over the main surfaceof the p type well, an n channel type MISFETQn is formed using similarsteps to those employed for the formation of a horizontal MISFET, whichwill be described later, and a p channel type MISFETQp is formed by astep using an impurity having an opposite conductivity type (refer toFIG. 39). These MISFETs constitute various circuits for driving amemory, for example, an X decoder (Xdec) or a Y decoder (Ydec), asillustrated in FIG. 36. In FIG. 36, PA represents a peripheral circuitregion, while MA represents a memory region.

Over the surface of the p type well 4, a gate insulating film 6 having athickness of about from 3 nm to 4 nm is formed. This gate insulatingfilm 6 is made of, for example, a silicon oxide film, and it is formedby thermal oxidation of the substrate 1.

Over the gate insulating film 6, a polycrystalline silicon film having,for example, an n type impurity doped therein is deposited as aconductive film, followed by deposition thereover of a silicon oxidefilm as a cap insulating film by, for example, chemical vapor deposition(CVD).

The above-described silicon oxide film is then patterned, and using thispatterned silicon oxide film as a mask, the n type polycrystallinesilicon film is dry etched to form gate electrodes 7A,7B over the p typewell 4.

Compared with a photoresist film, silicon oxide has a greater etchingselectivity to polycrystalline silicon so that by using silicon oxide asa mask, patterning of a minute gate electrode can be attained with goodaccuracy.

The gate electrode 7A constitutes a gate electrode of the transferMISFETs (TR1 and TR2), while the gate electrode 7B constitutes the gateelectrode of the drive MISFETs (DR1 and DR2). As illustrated in FIG. 3,the gate electrodes 7A,7B have a rectangular plane pattern extending inthe direction X, and their width in the direction Y, that is, the gatelength, is, for example, from 0.13 to 0.14 μm.

By ion implantation of an n type impurity (for example, phosphorous orarsenic) into the p type wells 4 on both sides of the gate electrodes7A,7B, an n⁻ type semiconductor region 9 having a relatively lowconcentration is formed. After successive deposition over the substrate1 of a silicon oxide film and a silicon nitride film, serving asinsulating films, by CVD, these films are anisotropically etched to formside wall spacers 13 on the side walls of the gate electrodes 7A,7B. Bythis anisotropic etching, the silicon oxide film over the gateelectrodes and the gate insulating film (silicon oxide film) 6 over thesurface of the substrate 1 are removed.

By ion implantation of an n type impurity (for example, phosphorous orarsenic) into the p type wells 4 on both sides of the gate electrodes7A,7B, n⁺ type semiconductor regions 14 having a relatively highconcentration are formed.

By the steps so far mentioned, the transfer MISFETs (TR1 and TR2) anddrive MISFETs (DR1 and DR2) having source and drain regions of an LDDstructure are formed. Of these four MISFETs, TR1 and DR1 have one of thesource and drain regions in common, and TR2 and DR2 have one of thesource and drain regions in common.

Over the substrate 1, a cobalt (Co) film is then deposited as a highmelting point metal film by, for example, sputtering, followed by heattreatment, whereby a silicide reaction is caused on the interfacebetween the Co film and the gate electrodes 7A,7B and the Co film andthe substrate 1 (n⁺ type semiconductor region 14), and a silicide layer18 is formed. Then, an unreacted portion of the Co film is removed byetching.

Over the MISFETs (TR1, TR2, DR1 and DR2), a silicon nitride film 19 anda silicon oxide film 20 are deposited as an insulating film by, forexample, CVD, and then, the surface of the silicon oxide film 20 isplanarized by chemical mechanical polishing (CMP).

Using a photoresist film as a mask, the silicon oxide film 20 andsilicon nitride film 19 are dry etched to form a contact hole 21 overthe gate electrode 7A of the transfer MISFETs (TR1 and TR2) and acontact hole 22 over the gate electrode 7B of the drive MISFETs (DR1 andDR2). In addition, contact holes 23,24,25 are formed over the source anddrain (n⁺ type semiconductor regions 14) of each of the transfer MISFETs(TR1, TR2) and drive MISFETs (DR1, DR2). Of these, the contact hole 23is formed over the source and drain regions which are common to TR1 andDR1, and TR2 and DR2.

Over the silicon oxide film 20, including the insides of the contactholes 21 to 25, a laminate of a titanium (Ti) film and a titaniumnitride (TiN) film are deposited as a barrier film by, for example,sputtering. After deposition of a tungsten (W) film serving as aconductive film by, for example, CVD, the W film outside the contactholes 21 to 25 is removed by CMP, whereby a plug 28 is formed inside ofthe contact holes 21 to 25.

As illustrated in FIGS. 4 and 5, a silicon nitride film 29 and a siliconoxide film 30 are successively deposited as an insulating film over thesubstrate 1 by, for example, CVD, followed by dry etching of thesefilms, whereby grooves 31 to 35 are formed over the contact holes 21 to25, respectively. Of these, the grooves 32 and 33 each extends from theupper part of the contact hole 22 toward the upper part of the contacthole 23. The silicon nitride film 29 serves as a stopper film uponetching of the silicon oxide film 30.

Over the silicon oxide film 30 including the insides of the grooves 31to 35, a TiN film is deposited to serve as a barrier film by, forexample, sputtering, followed by deposition of a W film serving as aconductive film by, for example, CVD. The W film outside the grooves 31to 35 is then removed by CMP to form intermediate conductive layers 41to 45. FIG. 6 illustrates a fragmentary plan view of a memory cell arrayafter the formation of the intermediate conductive layer. As describedabove, cell regions are disposed in an array in the X and Y directions,and each cell region is disposed axisymmetric to a short side of thecell region running in the Y direction and axisymmetric to a long sideof the cell region running in the X direction. Each pattern in the cellregion is disposed point-symmetric to the central point of the cellregion.

Of the intermediate conductive layers 41 to 45 shown in FIG. 5, the pairof intermediate conductive layers 42,43 formed at almost the center ofthe memory cell region correspond to the storage nodes A,B of FIG. 1.

More specifically, the intermediate conductive layer 42(A) iselectrically connected to the source and drain regions (n⁺ typesemiconductor regions 14) common to TR1 and DR1 and the gate electrode7B of DR2, while the intermediate conductive layer 43(B) is electricallyconnected to the source and drain regions (n⁺ type semiconductor regions14) common to TR2 and DR2 and the gate electrode 7B of DR1.

Over the intermediate conductive layers 42(A) and 43(B), verticalMISFETs (SV1) and (SV2) are then formed, respectively. The gateelectrode of SV1 is connected to the intermediate conductive layer 43(B)and the gate electrode of SV2 is connected to the intermediateconductive layer 42(A).

In addition, a word line (WL) is formed over the intermediate conductivelayer 41, bit lines (BLT, BLB) are formed over the intermediateconductive layer 44, and a reference voltage (Vss) line is formed overthe intermediate conductive layer 45. Over the vertical MISFET, a supplyvoltage line (Vdd) is formed.

The steps employed in the manufacture of the vertical MISFET and variousinterconnects will be described next.

In the fragmentary plan views of FIGS. 7 to 32, in order to facilitatean understanding of the drawings, patterns of layers below theintermediate conductive layer are omitted.

As illustrated in FIGS. 7 and 8, for example, a WN film is depositedover the surfaces of the intermediate conductive layers 42,43 bysputtering, followed by patterning, whereby a barrier layer 48 isformed. This barrier layer 48 is formed to prevent the occurrence ofundesired silicide reaction on the interface between a silicon filmconstituting a plug 55 and the intermediate conductive layers 42,43.Therefore, it may be formed only over the formation region of the plug55.

After deposition of a silicon nitride film 49 as an insulating film overthe substrate 1 by, for example, CVD, a polycrystalline silicon film (oramorphous silicon film) having a p type impurity doped therein isdeposited as a conductive film by, for example, CVD over the siliconnitride film.

By patterning the polycrystalline silicon film, a pair of gateextraction electrodes 51 (51 a,51 b) are formed. The gate extractionelectrodes 51 are disposed in a region adjacent to the plane patterns ofthe vertical MISFETs (SV1,SV2), which will be formed later, and they areconnected to the gate electrode (66) of the vertical MISFETs (SV1,SV2).The gate extraction electrodes 51 a,51 b are disposed in the vicinity ofthe intermediate conductive layers 42,43, respectively.

Formation of the plug 55 to be connected to the vertical MISFET and thegate extraction electrodes 51 a,51 b at the above-described positions inalmost the same layer makes it possible to connect the gate extractionelectrode to the gate electrode in self alignment and, moreover, toreduce the vertical difference between the gate extraction electrode andthe intermediate conductive layers 42,43, making it possible to connectthem via a tungsten (W) plug 80, which will be described later.

As illustrated in FIG. 9, a silicon oxide film 52 is deposited as aninsulating film over the silicon nitride film 49 by, for example, CVD tocover the gate extraction electrode 51. The silicon oxide film 52 overthe barrier layer 48 is then dry etched to form a through-hole 53. Thesilicon nitride film 49 functions as a stopper film during etching ofthe silicon oxide film 52.

A silicon oxide film is deposited by CVD over the silicon oxide film 52,including the inside of the through-hole 53, followed by anisotropicetching of the silicon oxide film to form, over the side walls of thethrough-hole 53, side wall spacers 54 made of an insulating film. Bythis anisotropic etching, the silicon nitride film 49 at the bottom ofthe through-hole 53 is also etched.

After deposition, over the silicon oxide film 52 including the inside ofthe through-hole 53, of a polycrystalline silicon film (or amorphoussilicon film) having a p type impurity doped therein, by, for example,CVD, the polycrystalline silicon film outside the through-hole 53 isremoved by CMP (or etch back) to form the plug 55 inside of thethrough-hole 53.

Over the silicon oxide film 52 including the upper part of the plug 55,a p type silicon film 57 p, a silicon film 58 i and a p type siliconfilm 59 p are formed. These three layers of silicon films (57 p, 58 i,59 p) are formed, for example, in the following manner. After successivedeposition of an amorphous silicon film having boron doped therein and anon-doped amorphous silicon film by CVD, these amorphous silicon filmsare heat treated to crystallize the same. After ion implantation intothe silicon film 58 i of an n type or p type impurity for the channelformation, an amorphous silicon film having boron doped therein isdeposited over the silicon film 58 i by CVD, followed by crystallizationof the resulting amorphous silicon film by heat treatment. Over the ptype silicon film 59 p, a thin silicon oxide film 61 and a siliconnitride film 62 are deposited over the p type silicon film 59 psuccessively as a cap insulating film by, for example, CVD.

As illustrated in FIGS. 10 and 11, using an unillustrated photoresistfilm as a mask, the silicon nitride film 62 is dry etched to leave thesilicon nitride film 62 over a region in which the vertical MISFETs(SV1, SV2) are to be formed. Using the silicon nitride film 62 as amask, the three silicon films (57 p, 58 i, 59 p) are dry etched, wherebycolumnar laminates (P1, P2) having a lower semiconductor layer(semiconductor region) 57 made of the p type silicon film 57 p, anintermediate semiconductor layer 58 made of the silicon film 58 i and anupper semiconductor layer 59 made of the p type silicon film 59 p areformed. At this time, the silicon nitride film 62 still remains over theupper semiconductor layer 59.

The lower semiconductor layer 57 of the laminate (P1) constitutes thedrain of the vertical MISFET (SV1), while the upper semiconductor layer59 constitutes the source of it. The intermediate semiconductor layer 58existing between the lower semiconductor layer 57 and the uppersemiconductor layer 59 substantially constitutes the substrate of thevertical MISFET (SV1) and its side walls constitute the channel regions.The lower semiconductor layer 57 of the laminate (P2) constitutes thedrain of the vertical MISFET (SV2) and the upper semiconductor layer 59constitutes the source of it. The intermediate semiconductor layer 58substantially constitutes the substrate of the vertical MISFET (SV2) andits side walls constitute the channel regions.

In this Embodiment, a transfer pattern (reticle pattern), uponpatterning of a photoresist film used for etching of the silicon nitridefilm 62, is formed to have a shape as illustrated in FIG. 12. Asillustrated in FIG. 12, this transfer pattern (which may be called a“transfer mask”) is H-shaped when viewed from the Y direction. Asdescribed later based on FIGS. 13(a) and 13(b), this transfer pattern(transfer mask) is H-shaped, more specifically, it does not have auniform width in the Y direction and is narrower at the center thereofthan a both ends. In FIG. 12, the patterns of the intermediateconductive layers 42,43 are also shown in order to facilitate anunderstanding of the positional relationship between the pattern of anactual device and the transfer pattern.

According to this embodiment, use of a transfer mask which has beenH-shaped in the Y direction enables etching of the photoresist film intoan approximately elliptical etching pattern having a longer diameter inthe X direction. By etching the silicon nitride film 62 through thisapproximately elliptical etching pattern and then, etching the columnarlaminates (P1, P2) through the resulting silicon nitride film 62 thusetched into an approximate ellipse, it is possible to make the planepattern of the columnar laminates (P1, P2) into an approximatelyelliptical shape that is longer in the X direction (refer to FIG. 17).Since the transfer mask which has been H-shaped in the Y direction isused, an approximately elliptical etching pattern having a longerdiameter in the X direction can be formed, and the columnar laminates(P1,P2) can be formed to have an approximately elliptical shape that islonger in the X direction.

As a result, the distance between any two adjacent columnar laminates inthe Y direction can be narrowed, making it possible to increase thechannel region (channel current) of the vertical MISFET while attainingminiaturization of a cell region.

Examples (a) and (b) in FIG. 13 show the relationship between thetransfer pattern and the etched shape (plane pattern of the laminate).As illustrated by Example (b), the transfer pattern is H-shaped in the Ydirection.

In other words, a rectangle having a short side (300 nm) and a long side(320 nm) lacks, at both ends at the center of the two long sides(direction X), a rectangular pattern having a predetermined width (120nm) in the X direction and a predetermined depth (70 nm) in the Ydirection. In short, the transfer pattern is H-shaped with its width inthe Y direction being narrower, at the center of the X direction, thanboth ends of the pattern.

When the transfer pattern having the above-described size is used, theplane pattern of the laminate is elliptical with a longer diameter ofabout 270 nm and a shorter diameter of about 230 nm.

When a square transfer pattern 240 nm on a side as illustrated byExample (a) is used, on the other hand, the plane pattern of thelaminate does not become a complete circle but is approximately circular(longer diameter: 236 nm, shorter diameter: 224 nm).

In the plain views and perspective views other than FIG. 17, a planepattern of each of the silicon nitride film 62 and columnar laminates(P1, P2) is illustrated as a rectangular one for convenience sake.

Upon dry etching of the above-described silicon films (57 p, 58 i, 59p), a taper may be formed on the bottom of the side walls of thelaminates (P1, P2), as illustrated in FIG. 10. An increase in thecontact resistance between the lower semiconductor layer 57 and the plug55 due to misalignment can be suppressed by the formation of a taper.

Upon forming the laminates (P1, P2), a thin (several nm or less) tunnelinsulating film composed of a silicon nitride film or the like may bedisposed in the vicinity of the interface between the uppersemiconductor layer 59 and the intermediate semiconductor layer 58, inthe vicinity of the interface between the lower semiconductor layer 57and the intermediate semiconductor layer 58, or at the center of theintermediate semiconductor layer 58. Provision of this tunnel insulatingfilm makes it possible to prevent diffusion of an impurity in the lowersemiconductor layer 57 or in the upper semiconductor layer 59 to theinside of the intermediate semiconductor layer 58.

As illustrated in FIGS. 14 and 15, a gate insulating film 63 is formedover the surface of the side walls of the lower semiconductor layer 57,intermediate semiconductor layer 58 and upper semiconductor layer 59,which layers constitute each of the laminates (P1, P2). This gateinsulating film 63 is made of, for example, a silicon oxide film and isformed by subjecting the substrate 1 to low-temperature thermaloxidation (for example, wet oxidation) at 800° C. or less. Since thesilicon oxide film 61 has been formed between the laminates (P1, P2) andthe silicon nitride film 62 thereover, contact between the gateinsulating film 63 formed on the surface of the upper semiconductorlayer 59 with the silicon nitride film 62 can be prevented, and,therefore, lowering in the withstand pressure of the gate insulatingfilm 63 in the vicinity of the upper end portion of the laminates (P1,P2) can be prevented. The gate insulating film may be formed of adeposited film.

After a first polycrystalline silicon film 64, having a p type impuritydoped therein, is deposited as a conductive film over the silicon oxidefilm 52 and columnar laminates (P1, P2) by using, for example, CVD, thispolycrystalline silicon film is anisotropically etched to leave thefirst polycrystalline silicon film so as to surround therewith the sidewalls of the columnar laminates (P1, P2) and silicon nitride film 62. Byforming the first polycrystalline silicon film 64, which partiallyconstitutes the gate electrode (66), as described above in selfalignment, the memory size can be reduced. Upon etching of thispolycrystalline silicon film 64, the silicon oxide film 52 lyingtherebelow is etched successively.

As illustrated in FIGS. 15 and 16, a second polycrystalline silicon film65 having a p type impurity doped therein is formed, as a conductivefilm, over the surfaces of the silicon nitride film 49 and firstpolycrystalline silicon film 64 by, for example, CVD. By anisotropicetching of this polycrystalline silicon film, the second polycrystallinesilicon film 65 is left so as to surround therewith the surface of thefirst polycrystalline silicon film 64.

The second polycrystalline silicon film 65 is also formed over thesurfaces of the gate extraction electrodes 51 (51 a, 51 b) and it iselectrically connected to the gate extraction electrodes 51. The secondpolycrystalline silicon film 65 is also formed in self alignment so thatthe memory size can be reduced.

By the steps so far mentioned, the gate electrode 66 of the verticalMISFETs (SV1, SV2), that is made of a laminate of the firstpolycrystalline silicon film 64 and the second polycrystalline siliconfilm 65, is formed so as to cover the columnar laminates (P1, P2) andthe silicon nitride film 62.

FIG. 17 is a fragmentary plan view illustrating the relationship betweenthe columnar laminate and gate electrode in the memory cell array(plural cell regions). FIG. 18 is a schematic fragmentarycross-sectional view of the vertical MISFET after formation of the gateelectrode 66, in which the left diagram is a view taken along a lineX-X′ of FIG. 17, while the right diagram is a view taken along a lineY-Y′ of FIG. 17. In cross-sectional views of FIGS. 18 to 27, layersbelow the plug 55 are omitted. Some films, such as gate insulating film63, are also omitted. The gate extraction electrodes 51 (51 a, 51 b) areformed at a position lower than the lower semiconductor layer 57, but inthese diagrams, they are illustrated adjacent to the lower semiconductorlayer 57. FIG. 19 is a fragmentary perspective view illustrating thestate of the gate electrode 66 covering the side walls of the columnarlaminate in the memory cell array (in the perspective view, the gateextraction electrode is omitted. This will equally apply to FIGS. 22 and26).

As illustrated in FIG. 17, patterns each made of the columnar laminate(P1 or P2) and gate electrode 66 are disposed in the array form in the Xand Y directions. They are spaced by, for example, 1000 to 1200 nm (forexample, about 1040 nm) in the X direction, while the spacing (pitch) inthe Y direction is 60 nm. With regard to the arrangement of the columnarlaminate and gate electrode, there exist, for example, narrow pitchportions (D1) of 150 nm or less and wide pitch portions (D2) of 500 nmor greater.

Supposing that the lower semiconductor layer 57, intermediatesemiconductor layer 58, upper semiconductor layer 59 and silicon nitridelayer 62 constituting the columnar laminate are 300 nm, 300 nm, 300 nmand 300 nm thick, respectively, the height of the columnar laminatebecomes about 1200 nm. The aspect ratio of the narrow pitch portion isabout 20. When the aspect ratio of the narrow pitch portion exceeds 3,it becomes difficult to fill an insulating film between the adjacent twocolumnar patterns (P1, 66) with good accuracy. When the aspect ratioexceeds 6, an insulating film cannot be filled with good accuracy evenif a conventional technique for filling in a spacing betweeninterconnects or an isolation groove is employed. The aspect ratio ofthe wide pitch portion, on the other hand, becomes about 1. At thispoint, a step of filling an insulating film between a plurality ofcolumnar patterns (P1, 66) having both a narrow pitch portion and a widepitch portion will be described.

As illustrated in FIGS. 20 to 22, a first insulating film 70 a havinggood coverage is deposited. A so-called TEOS film can be given as anexample of a film having good coverage. This TEOS film is a film formedby CVD using tetraethoxysilane (Si(OC₂H₅)₄) as a raw material. Examplesinclude an O₃-TEOs film obtained by using an active oxidizing speciessuch as ozone (O₃) as another raw material to heighten the reactivity ofthe film, and a P-TEOS film whose reaction is carried out under a plasmaatmosphere.

The O₃-TEOS film has better coverage than the p-TEOS film so that it issuited as the first insulating film 70 a.

Examples of another film having good coverage include thermal CVD filmsobtained by monosilane or disilane as a raw material and which can bemade reactive by heat. In this case, however, heat treatment at 700° C.or greater (preferably 800° C.) for about 10 hours is necessary, and sodeterioration in device properties due to thermal stress is inevitable.In the manufacture of a miniaturized and highly-integrated device, suchas the SRAM of the present invention, there exists a thermal stressstandard of limiting application of a thermal stress to a predeterminedtime in terms of a standard temperature throughout the manufacturingsteps. It is difficult to satisfy this thermal load standard when thethermal CVD film is employed.

The O₃-TEOS film, on the other hand, can be formed at 700° C. or less sothat a film with good coverage is available while reducing the thermalstress in the manufacturing steps.

The following is one example of the film forming conditions of anO₃-TEOS film. It is formed under conditions of a TEOS flow rate of from800 to 2000 mgm (milligram per minute), an O₃ flow rate of from 5000 to10000 sccm, a nitrogen (N₂) flow rate of from 8000 to 20000 sccm, atemperature from 450 to 600° C., and a subnormal pressure of 600 Torr (1Torr=1.33322×10² Pa) while using tetraethoxysilane (TEOS) and O₃ as rawmaterials. Spacing from a susceptor for loading a wafer thereon and ashower head portion which is a raw material gas feeding part is, forexample, from 200 to 400 mils. The pressure may fall within a range offrom 20 to 760 Torr.

The P-TEOS film is formed under the conditions, for example, of 300° C.and an atmosphere of about 5 to 10 Torr, while using tetraethoxisilaneand oxygen as raw materials.

After formation of the first insulating film (O₃-TEOS film) 70 a, it maybe heat treated at, for example, 700° C. for 1 minute in order todensify the film.

As illustrated in FIG. 21, the first insulating film 70 a is thickenough to fill therewith narrow pitch portions completely, but notenough to fill wide pitch portions. More specifically, after formationof the first insulating film 70 a, a concave portion 170 is formed overa wide-pitch space. The thickness of the first insulating film 70 a isadjusted to the narrow-pitch space (D1=60 nm) or greater inconsideration of variations in the size between the pitches or themargin of the film thickness. The upper space between the two adjacentcolumnar patterns (P1, 66) is wider than the bottom space (refer to FIG.16).

In order to reduce the generation of voids in such a portion andmaintain a thickness to some extent over the columnar pattern, the filmthickness is preferably adjusted to at least a thickness of the narrowpitch portion (in this case, about 200 nm) between the two adjacentpatterns, each made of the lower semiconductor layer 57, intermediatesemiconductor layer 58 and upper semiconductor layer 59. The thicknessof this first insulating film is, for example, based on a film existingover the wide pitch portion. It is also possible to form the firstinsulating film in portions and finally make it totally thick enough tofill the narrow pitch portion.

As another example, as illustrated in FIG. 22, a row of the columnarlaminates (P1, P2) and gate electrode 66 in the Y direction is coveredwith the first insulating film 70 a as if patterns 172 having a width ofabout 700 nm and thickness of about 1200 nm are spaced by about 800 to1000 nm (FIG. 20). The film thickness of the gate electrode 66 is about40 to 90 nm, while the thickness of the first insulating film over thewide-pitch portion is about 200 to 300 nm.

As illustrated in FIG. 23, a second insulating film 70 b is depositedover the first insulating film 70 a. Since the underlying layer of thissecond insulating film 70 b has a line pattern with a relatively largewidth and space, flatness is an important factor for it. When the secondinsulating film shows a conformal growth, irregularities of theunderlying layer (first insulating film 70 a) appear as irregularitiesof the second insulating film as is, which will cause a problem in thesubsequent steps, such as during CMP.

As the second insulating film 70 b, use of an insulating film formed byhigh-density plasma CVD (which will hereinafter be called “HDP film”) isrecommended.

The high density plasma CVD is a method of forming a film by reacting araw material gas under the atmosphere of high density (10¹¹/cm² orgreater) plasma. Upon reaction, an RF bias is applied to the substrate.In this high density plasma CVD, reaction is accelerated by the plasma,while sputter etching due to collision of the plasma with a depositedfilm occurs. This etching phenomenon occurs preferentially at theprotruded portion of the film. When an HDP film is employed as thesecond insulating film 70 b, its surface is not easily influenced by theirregularities of the underlying layer so that flatness can be secured(FIG. 23).

Here, an HDP silicon oxide film is employed. It is formed, for example,under conditions of an SiH₄ flow rate of from 70 to 90 sccm, an O₂ flowrate of from 130 to 170 sccm, an argon (Ar) flow rate of from 350 to 450sccm, and a temperature of from 280 to 400° C. while using silane (SiH₄)and oxygen (O₂) as raw materials. LF is from 3000 to 4000 W, while HF isfrom 2000 to 3000 W. This generates a high density Ar/O₂/SiH₄ plasma.

Also, upon formation of this HDP film, the temperature is adjusted to700° C. or less in order to reduce the thermal stress.

In order to fill the second insulating film 70 b to a certain depth ofthe concave portion 170 over the wide pitch portion, it is deposited toa film thickness corresponding to 70% or greater of a verticaldifference (H) between the bottom portion of the first insulating film70 a in the wide pitch portion and the top( ) portion existing over thecolumnar laminates (P1, P2). Here, the thickness of the secondinsulating film is adjusted to about 600 to 1400 nm. This secondinsulating film may be formed in portions.

The vertical difference (H) is almost the height of the columnarlaminate (lower semiconductor layer 57, intermediate semiconductor layer58, upper semiconductor layer 59 and silicon nitride film 62) in FIG.23. When the plug 55 is formed below the lower semiconductor layer 57,the height of the plug 55 is also included in the vertical difference(refer to FIG. 16).

Examples of the high-density plasma CVD include electron cyclotronresonance plasma (ECR) CVD, capacitively coupled plasma (IPC) CVD andhelicon plasma CVD. For the formation of an HDP film, a manufacturingapparatus for a semiconductor device having, as a plasma source,microwaves, helicon waves, ICP, ECR or the like is used.

Phosphorous or boron may be doped into the first insulating film(O₃-TEOS film) 70 a to make it a BPSG or PSG film. Fluorine orphosphorous may be doped into the second insulating film (HDP film) 70b. Thus, gettering effects are available by doping an impurity in aninsulating film.

According to this Embodiment, it is possible to fill the space betweencolumnar patterns with good accuracy, because after the first insulatingfilm having good coverage is deposited with a thickness sufficient tocompletely fill the narrow pitch portions, the second insulating film isdeposited thereover. As illustrated in FIG. 40, when a single layer ofthe O₃-TEOS film 70 a is formed to a film thickness of about 1 μm inorder to fill the wide pitch portions of the columnar patterns (P1, 66)to some extent, a film of about 1 μm thick is inevitably deposited overthe columnar patterns owing to excessively good coverage, which cause amarked increase in the surface irregularities. As a result, the flatnessover the film cannot be maintained by polishing.

When the O₃-TEOS film 70 is deposited to a thickness of 1 μm or greater,foreign matter generally tends to appear in a chamber (reactionchamber). The greater the amount of the foreign matter, the higher thefrequency of maintenance of the film forming apparatus, leading to alowering in the productivity. Accordingly, countermeasures against it,for example, formation of an O₃-TEOS film of about 500 nm thick twice isnecessary, which makes the manufacturing steps cumbersome.

The film formation rate of the O₃-TEOS film is slow and about 12 hoursis needed for the deposition of a film having a thickness of about 1 μm.

Judging from this, filling of the space between the columnar patternswith a single layer of the O₃-TEOS film is very difficult.

An ordinarily employed HDP film, on the other hand, tends to cause voidswhen the spacing is 100 nm or less and the aspect ratio is 3 or greater.It is accordingly difficult to fill the space between columnar patternswith a single layer of an HDP film.

Even if the film forming conditions can be adjusted (for example, byincreasing a bias power) to improve the filling properties, it bringsabout another problem such as a rise in the etching amount of theexposed gate electrode 66 or silicon nitride film 62 owing to anincrease in the sputtering component.

In addition, the charge-up damage of the exposed gate electrode isincreased, leading to a deterioration in device properties.

In this embodiment, on the other hand, an HDP film is used as the secondinsulating film 70 b. Upon formation of this film, the gate electrode 66has been covered with the first insulating film 70 a so that an etchingor charge-up problem of the gate electrode due to a sputtering componentcan be overcome.

Filling, with a P-TEOS film 270 d, of the concave portion on the surfaceof the O₃-TEOS film 70 a as illustrated in FIG. 40 can also be given asone countermeasure (FIG. 41). Also, in this case, the surface roughnessis large, which may presumably cause an increase in the verticaldifference between the memory region (memory cell array) MA andperipheral circuit region PA or a vertical difference between the memoryregion and a space between a plurality of memory mats MM or memoryblocks MB formed in the memory cell array. In the peripheral circuitregions, elements are not formed densely, or over the space betweenmemory mats or memory blocks, almost no pattern but only the O₃-TEOSfilm and P-TEOS film are formed. In the memory cell array, on the otherhand, these films are deposited over the columnar patterns. This causesa vertical difference of about 1 μm.

On the other hand, the HDP film (70 b) is employed in this embodiment.The film component over the columnar pattern is preferentially etched sothat only a thin film is formed over the protruded portion. This makesit possible to reduce the vertical difference between the memory cellarray and the peripheral circuit region, or a vertical differencebetween the memory cell array and a space between a plurality of memorymats formed in the memory array. FIG. 39 is a fragmentarycross-sectional view of the memory cell array (left side) and theperipheral circuit region (right side) after the formation of the HDPfilm (70 b). In the left side diagram of FIG. 39, layers below the lowersemiconductor layer 57 are omitted. In the right side diagram,interconnects or plugs between Qn and Qp, and the first insulating film70 a are omitted. The devices Qn and Qp are MISFETs constituting variouscircuits for driving the memory. The relationship among the peripheralcircuit region PA, memory region MA, memory mat MM and memory block MBis shown in FIG. 36.

FIG. 37 is a fragmentary plan view of the substrate illustrating oneexample of the layout of the columnar laminate (P) at the boundary ofthe memory mats MM; and FIG. 38 is a fragmentary plan view of thesubstrate illustrating one example of the layout of the columnarlaminate (P) at the boundary of the memory blocks MB. In FIG. 37, thedistance between the columnar laminates (P) at the boundary of MM in theX direction is about 1.62 μm, while that in the Y direction is about 1.5μm. In FIG. 38, the distance between the columnar laminates (P) at theboundary of MB in the X direction is about 20 μm.

The approximately square patterns in these diagrams correspond to a plug80, which will be described later. Also between MMs or MBs,approximately square patterns (plugs) for, for example, well feed aredisposed.

The distance between any two adjacent MMs or MBs is not limited to theabove-described one, and they may be spaced more narrowly or morewidely, depending on the layout.

What is important here is that use of the HDP film (70 b) makes itpossible to maintain the flatness of a film over the memory cell arrayand, at the same time, to narrow the above-described vertical differenceby depositing a film of a similar thickness over the peripheral circuitregion or space between memory mats.

After formation of a thin O₃-TEOS film, a P-TEOS film may be formedthereover. When the O₃-TEOS film is formed to a thickness as thin asthat shown in FIG. 21, however, the concave portion 170 cannot be filledwith the P-TEOS film with good accuracy, and slit voids appear in thefilm. The O₃-TEOS film must be as thick as 600 nm or greater in order toavoid generation of such voids and if so, similar problems which occurwhen a single layer of the O₃-TEOS film is used for filling.

According to this Embodiment, on the other hand, the space betweencolumnar patterns can be filled with good accuracy as described above.An insulating film can be filled with good accuracy even if a narrowspace portion has an aspect ratio of 3 or greater.

As illustrated in FIG. 24, after deposition of a P-TEOS film, as thethird insulating film 70 c, over the second insulating film 70 b, thesurface of the P-TEOS film is polished by CMP to planarize the same.

As illustrated in FIGS. 25 and 26, the first to third insulating films70 a to 70 c are etched to withdraw their surfaces, whereby portions ofthe columnar laminates (P1, P2) on and above a predetermined height areexposed. The term “predetermined height” means a height at which atleast the gate electrode 66 over the side walls of the uppersemiconductor layer 59 is exposed. In other words, the “predeterminedheight” is a position between the bottom and the top of the uppersemiconductor layer 59.

Indicated at numeral 172 a in FIG. 26 is a projecting portion of thefirst insulating film 70 a after this etching, and from this projectingportion, a portion and upper portion of the columnar laminates (P1, P2),and the gate electrode 66 over the side walls thereof are protruded.

The surfaces of the second insulating film and the first insulating filmmay be withdrawn by etching while carrying out neither deposition of thethird insulating film 70 c nor CMP. This step of withdrawing the surfaceof these insulating films is an important step for controlling the etchback amount of the gate electrode 66, which will be described later.When etching is conducted without reducing the surface irregularities ofthe insulating film, the surface height tends to vary after etching.Etching after deposition of the third insulating film 70 c andplanarization of the surface thereof by CMP therefore facilitatescontrol of the etching amount. In short, it can improve thecontrollability of etch back of the gate electrode. Or, after depositionof the third insulating film 70 c and CMP are omitted and the surface ofthe second insulating film 70 b is planarized by CMP, the planarizedsurface may be etched.

When the third insulating film 70 c is deposited, some irregularitiesmay appear after the deposition of the second insulating film 70 b,because the third insulating film 70 c relieves the irregularities andCMP planarizes the surface. When the third insulating film is employed,it happens to remain even after this etching.

An excessively large vertical difference disturbs CMP so that the secondinsulating film is desirably deposited to give a film thickness of 70%or greater of the vertical difference (H) of the first insulating film70 a as described above.

When the third insulating film 70 c is not formed, the thickness of thesecond insulating film is adjusted so as to completely fill the concaveportion 170 over the wide pitch portion. Adjustment of the thickness ofthe second insulating film 70 b to at least about 1.5 times the verticaldifference (H) facilitates flatness control by CMP.

In the next place, the gate electrode 66 that is exposed over the sidewalls of the columnar laminates (P1, P2) is etched so that the upper endportion of the gate electrode will come at the side wall portions of theupper semiconductor layer 59.

Etching of the gate electrode 66 is conducted in order to expose anupper portion of the upper semiconductor layer 59, which will be asource of the vertical MISFET. The upper end portion of the exposed gateelectrode 66 is preferably located over the side wall portions of theupper semiconductor layer 59 in order to prevent a short circuit betweenthe exposed portion (plug 85) and gate electrode 66. The etching amountis controlled so as not to locate the upper end portion of the gateelectrode 66 below the upper semiconductor layer 59, in order to preventoffset between the gate electrode 66 and the upper semiconductor layer59.

By the steps so far described, formed are p-channel type verticalMISFETs (SV1, SV2) having laminates (P1, P2) each made of the lowersemiconductor layer (drain) 57, intermediate semiconductor layer(substrate) 58 and the upper semiconductor layer (source), the gateinsulating film 63 formed over the side walls of the laminates (P1, P2)and gate electrode 66.

As illustrated in FIG. 27, a silicon nitride film is deposited as aninsulating film over the second insulating film 70 b by, for example,CVD, followed by anisotropic etching, whereby side wall spacers 71 areformed over the exposed portion of the vertical MISFETs (SV1, SV2), thatis, the side walls of the gate electrode 66, the upper semiconductorlayer 59 and the silicon nitride film 62 thereover.

After deposition of a silicon oxide film 73 to serve as a fourthinsulating film over the second insulating film 70 b by, for example,CVD, the surface of the silicon oxide film 73 is planarized by CMP. Asthis fourth insulating film 73, a P-TEOS film, for example, is employed.The fourth insulating film 73 does not necessarily have coverage,because the aspect ratio of the narrowly spaced columnar patterns isreduced by the first and second insulating films. Use of, for example, aP-TEOS film is preferred from the viewpoint of a small thermal stressand a high film forming rate.

FIG. 28 is a fragmentary cross-sectional view of the substrate after theformation thereover of the silicon oxide film 73. This diagram includesunderlying MISFETS (DR1, DR2 and TR1). Indicated at numeral 70 is alaminate of the first insulating film 70 a and the second insulatingfilm 70 b.

As illustrated in FIGS. 29 and 30, using a photoresist film as a mask,the first, second and fourth insulating films (70 a, 70 b, 73) are dryetched, whereby a through-hole 74 having a bottom extending from thegate extraction electrode 51 a to the intermediate conductive layer 42and a through-hole 75 having a bottom extending from the gate extractionelectrode 51 b to the intermediate conductive layer 43.

At the same time, through-holes 76, 77 and 78 are formed, from which thesurfaces of the intermediate semiconductor layers 41, 44 and 45 areexposed, respectively are formed.

A Ti film and a TiN film are deposited as a barrier film over thesilicon oxide film 73 including the insides of the through-holes 74 to78 by, for example, sputtering, followed by deposition of a W film as aconductive film by for example, CVD. The W film outside the through-holeis removed by CMP to form a plug 80 inside of the through-holes 74 to78.

Via the plug 80 in each of the through-holes 74 and 75, the gateextraction electrodes 51 a and 51 b can be connected to the intermediateconductive layers 42 and 43 (storage nodes A, B), respectively. In otherwords, the gate electrodes of the two vertical MISFETs can becross-connected to the storage nodes A and B.

By the steps so far described, a memory cell having two transfer MISFETs(TR1, TR2), two drive MISFETs (DR1 and DR2) and two vertical MISFETs(SV1, SV2) is substantially completed.

After deposition of a silicon oxide film 81 to serve as an insulatingfilm over the silicon oxide film 73 by CVD, using a photoresist film asa mask, the silicon oxide films 81, 73 and silicon nitride film 62 overthe laminates (P1, P2) are removed by dry etching to expose the uppersemiconductor layer (source) 59 of the vertical MISFETs (SV1, SV2),whereby a through-hole 82 is formed.

The above-described dry etching is conducted as follows: First, when thesilicon oxide films 81,73 over the laminates (P1, P2) are removed,etching is terminated temporarily. Since the side wall spacers 71 thatare made of a silicon nitride film are formed over the side walls of theupper semiconductor layer 59, exposure of the gate electrode 66 can beprevented even if a misalignment of the photomask occurs. Next, thesilicon nitride film 62 is etched.

Then, the silicon oxide film 81 that is covering the upper portion ofthe plug 80 formed in the memory array is etched to form a through-hole84. A TiN film, for example, is deposited as a barrier film over thesilicon oxide film 81 including the insides of the through-holes 82,84by, for example, sputtering, followed by deposition of a W film to serveas a conductive film. The W film outside the through-holes 82,84 isremoved by CMP, whereby a plug 85 is formed inside of the through-holes82,84.

As illustrated in FIGS. 31 and 32, a silicon carbide film 86 and asilicon oxide film 87 are deposited successively, to serve as aninsulating film, over the silicon oxide film 81. Using a photoresistfilm as a mask, the silicon oxide film 87 and silicon carbide film 86over the through-hole 84 are dry etched to form an interconnect groove88.

Over the silicon oxide film 87, including the inside of the interconnecttrench 88, a tantalum nitride (TaN) film or a tantalum (Ta) film isdeposited as a barrier film by, for example, sputtering, followed bydeposition of a copper (Cu) film to serve as a conductive film bysputtering or plating. Then, an unnecessary portion of the Cu filmoutside the interconnect groove 88 is removed by CMP. Theseinterconnects will become a supply voltage line 90 (Vdd) andcomplementary data lines (BLT, BLB), and they will also become anextraction interconnect 92 existing at the end of the memory cell.

As illustrated in FIGS. 33 and 34, after a three-layer insulating film93 is deposited over the silicon oxide film 87, an interconnect groove94 is formed in the insulating film 93. Over the insulating film 93,including the inside of this interconnect groove 94, a Cu film and a TaNfilm are deposited in the above-described manner, followed by removal ofan unnecessary Cu film outside the interconnect groove 94 by CMP. Theinsulating film 93 is made of, for example, a laminate of a siliconoxide film, a silicon carbide film and a silicon oxide film deposited byCVD. Upon formation of the interconnect groove 94 in the insulating film93, an opening 94 a is formed in the interconnect groove 94 over each ofthe four extraction interconnects 92 formed at the end of the memorycell, and a Cu film is formed inside of this opening. Theseinterconnects are to serve as a reference voltage line 91 (Vss) and aword line (WL).

In the above-described SRAM memory cell, the columnar laminatesconstituting the vertical MISFET are formed to have an ellipticalpattern, but they may be formed to have an approximately rectangularpattern.

The underlying MISFETs (DR1, DR2, TR1, TR2) in the SRAM memory cell areable to have various planar layouts.

As described below, four MISFETs may be used for constituting an SRAMmemory cell.

In this case, drive MISFETS (DR1, DR2) are formed as a relatively lowerlayer of the memory cell; and, over the drain region, vertical MISFETs(SV, SV2) are formed. FIG. 42 is an equivalent circuit diagram of a SRAMmemory cell in this case. FIG. 43 is a fragmentary plan view of thismemory cell, FIG. 44 is a fragmentary cross-sectional view, in which theleft diagram is taken along a line A-A′ of FIG. 43, while the rightdiagram is taken along a line B-B′ of FIG. 43.

The drive MISFETS (DR1, DR2) in these diagrams can be formed in asimilar manner to that employed for the drive MISFETs illustrated inFIGS. 33 and 34.

Over the source and drain regions of these MISFETs, plugs (327, 341) areformed in contact holes (324, 340). A reference voltage line 334 isdisposed over this plug 327, while vertical MISFETS (SV1, SV2) aredisposed over the plug 341 via a connecting conductive layer 346.

These vertical MISFETS each have a lower semiconductor layer 347, anintermediate semiconductor layer 348, an upper semiconductor layer 349,a gate insulating film 359 formed therearound and a gate electrode 354.

As illustrated in FIG. 45, there is a difference between a space 3D1, inthe X direction, of the vertical MISFETs (SV1, SV2) constituting thememory cell array and a space 3D2 in the Y direction. The latter spaceis greater. These spaces are filled with an insulating film 355 asillustrated in FIG. 44.

The insulating film is made of a two-layer insulating film, and, asillustrated in FIG. 46, the space is filled in two steps by, forexample, depositing a first insulating film 355 a and, then, a secondinsulating film 355 b in the space, successively. These insulating filmscan be formed in a similar manner to the first and second insulatingfilms 70 a,70 b. Of course, a third insulating film may be depositedover the second insulating film 355 b.

By filling an insulating film in two steps, it is possible to improvethe filling property of the insulating film, improve the withstandpressure, prevent a short circuit and improve the properties and yieldof the vertical MISFETs.

In the present memory cell, formation of the first and second insulatingfilms is followed by etching, formation of a word line WL and etch backof the gate electrode 354. Then, a plug (365) and interconnects (BLT,BLB) are formed.

These are a silicon nitride film 320, silicon oxide films 321 and 322, asilicon nitride film 328, a silicon oxide film 329, an interconnectgroove 331, a silicon nitride film 338, a silicon oxide film 342, agroove 356, a polycrystalline silicon film 357, side wall spacers 358, aCo silicide layer 360, a silicon oxide film 361, a plug 365, a siliconcarbide film 366, a silicon film 367 and an interconnect groove 368.Specific manufacturing steps of the SRAM memory cell illustrated in FIG.44 are described in Japanese Patent Application 2002-199308.

The memory cell (MC) of FIG. 42 has a structure in which a charge isretained by making use of leakage current (I_(OFF) (p)) at the time ofthe OFF state of the vertical MISFET (SV1 or SV2) made of a p channelMISFET.

The leakage current (I_(OFF) (p)) is greater than the leakage current(I_(OFF) (n)) of the drive MISFET (DR1 or DR2) which is OFF.

The various aspects and features of the present invention were describedspecifically based on the above-described embodiments. It should howeverbe borne in mind that the present invention is not limited to or by theabove-described embodiments, but can be changed to an extent notdeparting from the gist of the invention.

Particularly in the above-described embodiments, the description wasdirected to a SRAM memory cell as an example, but the present inventioncan be applied widely to semiconductor integrated circuit devices havingvertical MISFETs.

The SRAM memory cell is made of a plurality of MISFETs so that thelayout of the vertical MISFETs is limited by the layout of the otherMISFETS, which tends to cause a difference between vertical andhorizontal pitches of the vertical MISFETs.

Use of the filling method of the present invention is effective whensuch a difference appears between the vertical and horizontal pitches ofthe vertical MISFETs.

Advantages offered by the typical embodiments disclosed in the presentapplication, will next be described briefly.

In the columnar laminates of plural vertical MISFETs which are spaced bya first distance in a first direction and by a second distance, which isgreater than the first distance, in a second direction, the firstdistance portion is filled with a first insulating film and the seconddistance portion is filled with the first and second insulating films,which makes it possible to improve the filling properties of theinsulating films, to improve the properties of the semiconductorintegrated circuit device, and to attain miniaturization of thesemiconductor integrated circuit device.

Advantages available by the typical aspects of the inventions disclosedin the present application, will next be described briefly.

Filling properties of a space between the vertical MISFETs constitutingthe semiconductor integrated circuit device can be improved.

As another advantage, the properties of the semiconductor integratedcircuit device can be improved.

As a further advantage, miniaturization of the semiconductor integratedcircuit device can be attained.

1. A semiconductor integrated circuit device comprising a plurality ofvertical MISFETs, wherein the vertical MISFET comprises (a1) a columnarlaminate having, at the upper portion and lower portion thereof, a firstand second semiconductor regions, respectively, and (a2) a conductivefilm formed over the side walls of the columnar laminate via a firstinsulating film, wherein the plurality of vertical MISFETs having thecolumnar laminate and the conductive film are (b1) spaced by a firstdistance in a first direction, and (b2) spaced by a second distance,which is greater than the first distance, in a second direction, andwherein up to at least a predetermined height of the columnar laminateof the plurality of vertical MISFETs, (c1) a second insulating film isformed in a space between the columnar laminates in the first direction,and (c2) the second insulating film and a third insulating film lyingthereover are formed in a space between the columnar laminates in thesecond direction.
 2. A semiconductor integrated circuit device,comprising: a plurality of vertical MISFETs each including, (a1) acolumnar laminate having, at the upper portion and lower portionthereof, first and second semiconductor regions respectively, and (a2) aconductive film formed over the side walls of the columnar laminate viaa first insulating film, wherein said vertical MISFETs is arranged in anarray form, such that (b1) the vertical MISFETs are spaced by a firstdistance in a first direction, and such that (b2) vertical MISFETs arespaced by a second distance, which is greater than the first distance,in a second direction; (c) a second insulating film having, embeddedtherein, the vertical MISFETs aligned in the first direction, out of theplurality of vertical MISFETs, and having a plurality of projectingportions extending in the first direction; and (d) a third insulatingfilm formed between the plurality of projecting portions of the secondinsulating film.
 3. A semiconductor integrated circuit device accordingto claim 1, wherein the second insulating film has better coverage thanthe third insulating film.
 4. A semiconductor integrated circuit deviceaccording to claim 1, wherein the second insulating film is a siliconoxide film formed by chemical vapor deposition by usingtetraethoxysilane as a raw material, and the third insulating film is asilicon oxide film formed under a plasma atmosphere having a plasmadensity of 10¹¹ cm² or greater.
 5. A semiconductor integrated circuitdevice according to claim 4, wherein the second insulating film is asilicon oxide film formed by chemical vapor deposition by usingtetraethoxysilane and ozone (O₃) as raw materials.
 6. A semiconductorintegrated circuit device according to claim 1, wherein the columnarlaminate has a high at least 3 times as much as that of the firstdistance.
 7. A semiconductor integrated circuit device according toclaim 1, wherein the first distance is 150 nm or less, while the seconddistance is 500 nm or greater.
 8. A semiconductor integrated circuitdevice according to claim 1, wherein a fourth insulating film is filledin spaces, in the first direction and in the second direction, betweenthe columnar laminates on and above a predetermined height thereof.
 9. Asemiconductor integrated circuit device according to claim 1, wherein athickness of the second insulating film in the space between thecolumnar laminates in the second direction is the first distance orgreater.
 10. A semiconductor integrated circuit device according toclaim 1, wherein the plane pattern of the columnar laminate and theconductive film over the side walls thereof is approximately ellipticaland a first diameter in the first direction is smaller than a seconddiameter in the second direction.
 11. A semiconductor integrated circuitdevice according to claim 1, wherein the predetermined height existsbetween the bottom and top of the first semiconductor region.
 12. Asemiconductor integrated circuit device according to claim 1, whereinthe plurality of vertical MISFETs constitute a plurality of memory cellsdisposed in the array form in the first and second directions, thememory cells each including: (d1) of the plurality of vertical MISFETs,two vertical MISFETs adjacent in the first direction; (d2) twohorizontal drive MISFETs connected to the respective secondsemiconductor regions of the two vertical MISFETs, respectively, andtogether with the two vertical MISFETs, constituting a pair of invertershaving input and output portions cross-connected; and (d3) twohorizontal transfer MISFETs each connected between the secondsemiconductor region of each of the two vertical MISFETs and a firstline pair and having a gate electrode connected to a second line, (d4)wherein the two horizontal drive MISFETs and two horizontal transferMISFETs are formed below the second semiconductor region.
 13. Asemiconductor integrated circuit device according to claim 1, whereinthe plurality of vertical MISFETs constitute a plurality of memory cellsdisposed in the array form in the first and second directions, thememory cells each including: (d1) of the plurality of vertical MISFETs,two vertical MISFETs which are adjacent in the first direction, in whicheach has the second semiconductor region connected to a first line pair,and each has the conductive film connected to a second line; (d2) twohorizontal drive MISFETs connected between each of the secondsemiconductor regions of the two vertical MISFETs and a referencepotential, and having a gate electrode cross-connected to each of thesecond semiconductor regions of the two vertical MISFETs, (d3) whereinthe two horizontal drive MISFETs are formed below the secondsemiconductor region.
 14. A semiconductor integrated circuit deviceaccording to claim 12, wherein a single region in which the memory cellis formed is approximately rectangular and the length thereof is greaterin the second direction than that in the first direction. 15-33.(canceled)
 34. A manufacturing method of a semiconductor integratedcircuit device comprising a plurality of vertical MISFETs, wherein thevertical MISFET comprises (a1) a columnar laminate having, at the upperand lower portions thereof, first and second semiconductor regions,respectively, and (a2) a conductive film formed over the side walls ofthe columnar laminate via a first insulating film, wherein saidplurality of vertical MISFETs having the columnar laminate andconductive film are (b1) spaced by a first distance in a firstdirection, and (b2) spaced by a second distance, which is greater thanthe first distance, in a second direction, (c) the plane pattern of thecolumnar laminate and the conductive film over the side walls thereofbeing approximately elliptical, and a first diameter in the firstdirection being smaller than a second diameter in the second direction,the method comprising the steps of: (d) forming a semiconductor film,having at the upper and lower portions thereof, first and secondsemiconductor regions, respectively; and (e) etching the semiconductorfilm via a mask which is H-shaped in the first direction, therebyforming an approximately elliptical columnar laminate having a longerdiameter in a second direction perpendicular to the first direction. 35.A manufacturing method of a semiconductor integrated circuit deviceaccording to claim 33, wherein the steps are for the formation ofvertical MISFETs constituting a SRAM, and a single memory cell formationregion of the SRAM is approximately rectangular with a long side in thesecond direction.
 36. A semiconductor integrated circuit deviceaccording to claim 33, wherein the H-shaped mask is a transfer mask usedin photolithography, an approximately elliptical columnar pattern foretching is formed using the H-shaped transfer mask, and thesemiconductor film is processed into an approximately ellipticalcolumnar laminate by using the etching pattern.
 37. A semiconductorintegrated circuit device according to claim 36, wherein the H-shapedmask has a structure in which the width of the mask in the firstdirection is narrower at the center of the mask in the second directionthan at the both ends.
 38. A semiconductor integrated circuit device,comprising: (a) a columnar laminate having, at the upper and lowerportions thereof, first and second semiconductor regions, respectivelyand having an approximately elliptical plane pattern; and (b) aconductive film formed over the side walls of the columnar laminate viaan insulating film.
 39. A semiconductor integrated circuit devicecomprising a plurality of vertical MISFETs including: (a1) a columnarlaminate having, at the upper portion and lower portion thereof, firstand second semiconductor regions, respectively; and (a2) a conductivefilm formed over side walls of the columnar laminate via a firstinsulating film, wherein the plurality of vertical MISFETs having thecolumnar laminate and the conductive film are (b1) spaced by a firstdistance in a first direction, and (b2) spaced by a second distance,which is greater than the first distance, in a second direction, and (c)wherein a plane pattern of the columnar laminate and the conductive filmover the side walls thereof is approximately elliptical and a firstdiameter in the first direction is smaller than a second diameter in thesecond direction.
 40. A semiconductor integrated circuit deviceaccording to claim 38, wherein the columnar laminate constitutes thevertical MISFET of SRAM, and a single memory cell formation region ofthe SRAM is approximately rectangular and has a long side in thedirection of a longer diameter of the approximately elliptical shape.41. A semiconductor integrated circuit device according to claim 1,wherein the conductive film is formed to encompass the columnarlaminate.
 42. (canceled)